Korozija - Otporna na žicu za niobijum

Proizvodnja korozije - otporna niobijum-žica počinje topljenjem i pročišćavanjem visokog - čistoće niobijum metala. Pomoću procesa topljenja elektronskog snopa (EBM) i vakuumskih luka (VAR), čistoća niobijumskih sirovina povećana je na veću ili jednaku 99,95%, a sadržaj nečistoće poput kisika (o<100ppm) and nitrogen (N<50ppm) is strictly controlled. After the tube blank is preliminarily formed by hot extrusion, the wire diameter is gradually reduced to the target size through multiple cold drawing processes (with intermediate annealing), and the intermediate annealing is carried out in a vacuum environment of 800-1000 ° C to eliminate work hardening. The final wire diameter can be precisely controlled to be between 0.05-3.0mm with a tolerance of ± 0.005mm.
Da bi se poboljšala otpornost na koroziju, niobijum žica treba proći tretman površinske pasivicije. Dobivanje glatke površine (RA Manje od ili jednako 0,4 μ m) kroz elektrolitičko poliranje ili hemijsko poliranje promovira formiranje gustog niobijumskog pentoksida (NB ₂ O ₅). Prema posebnim zahtjevima, anodizirajuća liječenje može se koristiti za generiranje sloja debljine kontrole debljine (obično 1-5 μ m). Medicinska klasa Niobium žica također treba očistiti i pasivirati (poput dušične kiseline) kako bi se osigurala biokompatibilnost u skladu s ISO 5832 standardom.

 

 

Osnovne karakteristike

Izvrsna otpornost na koroziju

Ima odličnu otpornost na jake kiseline kao što su mitrična kiselina, hlorovodonična kiselina, aqua regia, te tečni metali (poput natrijuma i kalijuma), sa godišnjom brzinom korozije manjim od 0,01 mm (u okruženju od 70% aljom). Gusti niobijumski pentoksid (NB ₂ O ₅) Film sa pasivacijom formiran na njegovoj površini može učinkovito blokirati prodor korozivnih medija.


Biokompatibilnost i sigurnost

U skladu sa ISO 5832 i ASTM F2066 medicinskim standardima, ne {- toksičnim i ne-alergenim na ljudske tkive, otporne na karoziju tekućine tjelesne teku, pogodne za dugi - termin medicinski uređaji za implantaciju.

Stabilnost i mehanička svojstva visoke temperature

Talište je čak i 2468 stepena C, a održava dobru snagu i duktilnost u visokim temperaturnim i vakuumskim okruženjima, podržavajući složenu strukturnu obradu.


Obradavost i prilagodljivost

Izvrsna duktilnost, pogodna za preciznu obradu, poput hladnog savijanja, tkanja, zavarivanja itd.

Njegova jezgrena svojstva uključuju: otpornost na jaku kiselinu koroziju (godišnja stopa korozije<0.01mm in 70% nitric acid), biocompatibility (no cytotoxicity, no allergenicity), high melting point (2468 ° C), and good mechanical properties (tensile strength 400-1000 MPa, varying with wire diameter). Its density is 8.57 g/cm ³, with excellent ductility (elongation at break ≥ 15%), and supports precision machining such as weaving and bending.
Specifikacije proizvoda pokrivaju promjere žica od 0,05 - 3,0 mm, površinski glatkoću RA manji od ili jednak 0,4 μ m, a može pružiti prilagođena rješenja za različite stanja (mekane, tvrde) i površinske tretmane (poliranje, pasivizacija). Posebne aplikacije mogu zahtijevati dodatni tretmani za oblaganje (poput silikonskih premaza za poboljšanje otpornosti oksidacije). Niobijum-žica otporna na koroziju podvrgava strogim testiranjem kvaliteta, uključujući testiranje korozije (ASTM G48), testiranje biokompatibilnosti (ISO 10993) i nerazorno ispitivanje, kako bi se osigurala pouzdanost i dugovječnost u otežanim okruženjima kao što su hemijska, medicinska i morska sredina.
Niobijumska žica otporna na koroziju, sa odličnom jakom otpornošću na kiselinu (godišnja stopa korozije<0.01mm) and high temperature stability, has become an ideal material for resisting harsh environments in chemical equipment. The dense niobium pentoxide (Nb ₂ O ₅) passivation film formed on its surface can effectively resist the corrosion of nitric acid, hydrochloric acid and other media. For example, a large nitric acid production plant uses niobium wire woven reactor lining mesh, which has been continuously used for 3 years in a 70% nitric acid environment and at a temperature of 80 ° C without corrosion failure, and its service life is more than 5 times longer than traditional stainless steel. In addition, niobium wire is also used as an electrode connecting wire for electrolytic cells to maintain long-term conductivity stability in acidic electrolytes.
Biokompatibilnost (u skladu sa ISO 5832 standardom) i otpornošću na koroziju na tjelesne tekućine ovog materijala čine ga ključnim materijalom za medicinske implantate uređaje. Na primjer, žica za vaskularne intervencije napravljena je od 0,2 mm Niobium žice koja se u okruženju u krvi može dugo koristiti bez ionske padavine, a ima zatezna čvrstoća 800MPA, osiguravajući točnost i sigurnost hirurškog operacija. Neuralni poticaj elektroda koji je razvio međunarodno medicinsko preduzeće koristi konstrukcija tkanja niobijum-žice koja održava stabilnost u ljudskom tkivu više od 20 godina i efikasno izbjegava degradaciju performansi uzrokovanih korozijom tradicionalnih materijala.
U morskim okruženjima njen otpor kloridnom jonu koroziju značajno je bolji od većine metalnih materijala. Projekt od određenog morske vode koristi komponente filtra za tkane filtra niobijum žice, koje su koristile u visokim temperaturama i visokim solima u okruženju 5 godina bez pittiranja korozije ili pucanja na stres. U području nove energije, Niobium žica služi kao zaštitna mreža za rukav za mjerenje temperature u rastopljenim rektorima soli, sa kojim se sadrže 550 stupnjeva C tekuće rastične korozije i okruženja za ozračivanje; Projekt određenog protoka koristi kolektor za niobijum žice za održavanje elektrohemijske stabilnosti u kiselog elektrolita više od 10 godina.
Visoka čistoća (veća ili jednaka 99,95%) i čistoću površine korozije - otporne nibium žice ispunjava zahtjeve poluvodičkih procesa. Određeni proizvođač čipa koristi žicu od 0,1 mm kao žica za distribuciju plina CVD za održavanje dugog - termina stabilnosti u korozivnom plinskom okruženju na bazi fluora i izbjegavati kontaminiranje vafla. U polju vakuum peći, mreža za grijanje tkana sa niobijum žicom ne oslobađa zagađivače ili deformira pod visokom temperaturom i vakuumskom okruženju od 1800 stepeni C, osiguravajući pouzdanost procesa toplotnog obrade.
Niobijum žica otporna na koroziju pokazala je nezamjenjivu vrijednost u poljima poput hemijskog, medicinske, marine i poluvodičke industrije zbog svoje jedinstvene otpornosti na koroziju, biokompatibilnost i visok - stabilnost temperature. Praktični slučajevi primjene dokazali su da njegov radni vijek može dostići 3-5 puta od tradicionalnih materijala, značajno smanjenje troškova održavanja opreme i poboljšanje pouzdanosti sistema. Uz napredak tehnologija površinskih obrada, poput nano pasivacijskih filmova i kompozitnih premaza, granice aplikacije Niobium žice bit će dodatno proširiti na zahtjevnije okruženje.

Popularni tagovi: Korozija - otporna niobijumska žica, Kina korozija - otporni Niobium žičani proizvođači, dobavljači, tvornica, niob nb, Niobium 92, Niobium C103 Cijena, Cijena niobijum-metala, Niobium cijena oz, Tantalum metal za električne komponente